Energy-Dispersive X-Ray Spectrometry Analysis and Radiopacity of Five Different Root Canal Sealers

Root canal sealers should have optimum adhesion to the root dentin, low cytotoxicity, sufficient radiopacity and high dimensional stability, which depend mainly on their chemical composition. The aims of this study were to evaluate the chemical composition of Syntex (Cerkamed, Stalowa Wola, Poland), Adseal (Meta Biomed, Cheongju-si, Korea), Sealapex (SybronEndo, Scafati, Italy), MTA Fillapex (Angelus, Londrina, Brazil) and GuttaFlow Bioseal (Coltene/Whaledent, Altstätten, Switzerland) and to determine their radiopacity comparatively. Stainless steel molds with an inner diameter of 5 mm and a depth of 2 mm were constructed. Tested root-canal sealers were mixed and poured into the molds. Following setting, digital periapical radiographs of the specimens (n=12) were taken under standard exposure conditions and the mean gray-values of specimens were measured using a computer graphics program. Then the specimens were examined by scanning electron microscopy, and Energy-dispersive X-ray analysis was performed. The data were analyzed using One-way ANOVA followed by Holm-Sidak multi-comparison test (p = 0.05). Sealapex showed higher calcium peak than MTA Fillapex, GuttaFlow Bioseal, Adseal and Syntex sealers. MTA Fillapex contained a highest amount of tungstate. Sealapex presented the highest radiopacity value among the tested materials (p < 0.05), whereas MTA Fillapex was the least radiopaque material (p < 0.05). Each root canal sealer contains different compositions of radiopacifiers including bismuth oxide, calcium tungstate and zirconium oxide. The tested root canal sealers had radiopacity values above the ISO-specified limit. Sealapex was the most radiopaque root canal sealer followed by GuttaFlow Bioseal, Syntex, Adseal and MTA Fillapex.