Modification of cellulose from sugarcane (Saccharum officinarum) bagasse pulp by cold plasma: Dissolution, structure
Hong Zhu1, Zhuorui Han1, Jun-Hu Cheng1
1School of Food Science and Engineering, South China University of Technology, Guangzhou 510641, China; Academy of Contemporary Food Engineering, South China University of Technology, Guangzhou Higher Education Mega Centre, Guangzhou 510006, China; Engineering and Technological Research Centre of Guangdong Province on Intelligent Sensing and Process Control of Cold Chain Foods, & Guangdong Province Engineering Laboratory for Intelligent Cold Chain Logistics Equipment for Agricultural Products, Guangzhou Higher Education Mega Centre, Guangzhou 510006, China.
Abstract:
Cellulose is a most abundant natural biopolymer, however, the strong hydrogen bonding system makes cellulose hard to dissolve, limiting its further applications. In this study, an innovative cold plasma (CP) technology was used to modify cellulose from sugarcane (Saccharum officinarum) bagasse pulp. Dissolution, structure, and surface chemistry of cellulose before and after CP treatment were investigated. Results showed that the dissolution rate of cellulose after different CP treatment time (3-12 min) and operating voltage (40-70 kV) was significantly improved. Roughness, even holes (CP treatment 9 min with 50 kV) and breakage (CP treatment 9 min with 70 kV) were observed on the surface. The crystallinity index decreased from 62.31% (control) to 60.88% (CP treatment 3 min with 50 kV). The hydrogen bonding force was weakened and the peak intensity of CO and CO stretching vibration groups were enhanced. Therefore, CP-modified cellulose may be applied more in future, such as biological films for food future packaging.