Critical Redistribution of Nitrogen in the Austenitic Cr-Mn Steel under Severe Plastic Deformation

A narrow temperature range of changes in the mechanism and kinetics of structural-phase transformations during mechanical alloying under deformation in rotating Bridgman anvils was determined by the methods of Mössbauer spectroscopy, electron microscopy, and mechanical tests in the high-nitrogen chromium-manganese steel FeMn₂₂Cr₁₈N_0.83. The experimentally established temperature region is characterized by a change in the direction of nitrogen redistribution-from an increase in the N content in the metal matrix during cold deformation to a decrease with an increase in the temperature and degree of severe plastic deformation. The change in the direction of nitrogen redistribution is due to the acceleration of the decomposition of a nitrogen-supersaturated solid solution of austenite with the formation of secondary nanocrystalline nitrides. The presence of a transition region for the mechanism of structural-phase transitions is manifested in the abnormal behavior of the mechanical properties of steel.