Calcium Carbonate@silica Composite with Superhydrophobic Properties

In this paper, spherical calcium carbonate particles were prepared by using CaCl₂ aqueous solution + NH₃·H₂O + polyoxyethylene octyl phenol ether-10 (OP-10) + n-butyl alcohol + cyclohexane inverse micro emulsion system. Then, nanoscale spherical silica was deposited on the surface of micron calcium carbonate by Stöber method to form the composite material. Scanning electron microscope (SEM), X-ray powder diffraction (XRD), Fourier transform infrared spectroscopy (FTIR), Thermogravimetric analysis (TGA) and X-ray photoelectron spectroscopy (XPS) were used to characterize the morphology and structure of the composite material. It is found that the surface of the composite material has a micro-nano complex structure similar to the surface of a "lotus leaf", making the composite material show hydrophobicity. The contact angle of the cubic calcium carbonate, spherical calcium carbonate and CaCO₃@SiO₂ composite material were measured. They were 51.6°, 73.5°, and 76.8°, respectively. After modification with stearic acid, the contact angle of cubic and spherical CaCO₃ were 127.1° and 136.1°, respectively, while the contact angle of CaCO₃@SiO₂ composite was 151.3°. These results showed that CaCO₃@SiO₂ composite had good superhydrophobicity, and the influence of material roughness on its hydrophobicity was investigated using the Cassie model theory.