Corrosion behavior of HRB400 and HRB400M steel bars in concrete under DC interference

Qingmiao Ding1, Yuning Gao2, Ruiyang Liu1

  • 1Aeronautical Engineering Institute, Civil Aviation University of China, Tianjin, 300300, People's Republic of China.

Scientific Reports
|December 14, 2021
PubMed

More Related Videos

Applicability Analysis of Assessment Methods for Morphological Parameters of Corroded Steel Bars10:24

Applicability Analysis of Assessment Methods for Morphological Parameters of Corroded Steel Bars

Published on: November 1, 2018

6.8K
Metal Corrosion and the Efficiency of Corrosion Inhibitors in Less Conductive Media10:05

Metal Corrosion and the Efficiency of Corrosion Inhibitors in Less Conductive Media

Published on: November 3, 2018

18.1K

Related Concept Videos

Corrosion of Reinforcement01:27

Corrosion of Reinforcement

The corrosion of steel reinforcement within concrete is a process influenced by the material's inherent properties and external factors. The high pH level of around 13, provided by calcium hydroxide present in concrete, initially protects the steel reinforcement by promoting the formation of a passive iron oxide layer on its surface.
However, over time and under certain conditions like carbonation, chloride ingress, and cracking this protective state can be compromised. Steel has areas with...
290
Abrasion Resistance of Concrete01:23

Abrasion Resistance of Concrete

Abrasion resistance is an essential characteristic of concrete that determines its durability and longevity under various wear conditions. Concrete surfaces are vulnerable to different types of abrasion. For instance, surfaces may wear down due to the constant movement of vehicles or be eroded by solids carried in water, as seen in concrete canal linings. Specific tests are conducted to measure the abrasion resistance of concrete.
One such test is the revolving disc test, where three plates...
265
Reinforcements in Concrete01:25

Reinforcements in Concrete

Reinforced concrete is a composite material used extensively in construction, combining the compressive strength of concrete with the tensile strength of steel. This synergy is essential as concrete, while excellent at resisting compression, is weak under tension. Steel bars, or rebars, are embedded in the concrete to handle these tensile forces. The choice of steel is strategic; it shares a similar coefficient of thermal expansion with concrete, which ensures uniformity in response to...
207
Acid Attack on Concrete01:21

Acid Attack on Concrete

When acids come into contact with concrete, they initiate a chemical reaction that dissolves the hydrated cement paste. This process leads to softening and structural weakening of the concrete. This issue is commonly observed in environments such as chimneys, sewers, and industrial settings. The severity of the damage increases as the pH of the water interacting with the concrete drops below 6.5. In particular, a pH under 4.5 can cause significant concrete damage.
The rate at which hydrogen...
372
Corrosion02:49

Corrosion

The degradation of metals due to natural electrochemical processes is known as corrosion. Rust formation on iron, tarnishing of silver, and the blue-green patina that develops on copper are examples of corrosion. Corrosion involves the oxidation of metals. Sometimes it is protective, such as the oxidation of copper or aluminum, wherein a protective layer of metal oxide or its derivatives forms on the surface, protecting the underlying metal from further oxidation. In other cases, corrosion is...
25.9K
Behavior of Concrete Under Compressive Load01:23

Behavior of Concrete Under Compressive Load

Concrete exhibits specific behaviors under different compressive loads. Understanding this is crucial for understanding its structural integrity. When concrete undergoes uniaxial compression, it tends to develop cracks that run parallel to the direction of the force. These parallel cracks stem from localized tensile stresses that occur perpendicular to the compression direction. Additionally, angled cracks may appear due to the formation of shear planes.
As the concrete specimen fractures under...
321