Size-Dependent Chemomechanical Failure of Sulfide Solid Electrolyte Particles during Electrochemical Reaction with...

The very high ionic conductivity of Li₁₀GeP₂S₁₂ (LGPS) solid electrolyte (SE) makes it a promising candidate SE for solid-state batteries in electrical vehicles. However, chemomechanical failure, whose mechanism remains unclear, has plagued its widespread applications. Here, we report imaging lithiation-induced failure of LGPS SE. We revealed a strong size effect in the chemomechanical failure of LGPS particles: namely, when the particle size is greater than 3 μm, fracture/pulverization occurred; when the particle size is between 1 and 3 μm, microcracks emerged; when the particle size is less than 1 μm, no chemomechanical failure was observed. This strong size effect is interpreted by the interplay between elastic energy storage and dissipation. Our finding has important implications for the design of high-performance LGPS SE, for example, by reducing the particle size to less than 1 μm the chemomechanical failure of LGPS SE can be mitigated.