Investigation of Size Effects in Multi-Stage Cold Forming of Metallic Micro Parts from Sheet Metal

Product miniaturisation and functional integration are currently global trends to save weight, space, materials and costs. This leads to an increasing demand for metallic micro components. Thus, the development of appropriate production technologies is in the focus of current research activities. Due to its efficiency, accuracy and short cycle times, microforming at room temperature offers the potential to meet the steadily increasing demand. During microforming, size effects occur which negatively affect the part quality, process stability, tool life and handling. Within this contribution, a multi-stage bulk microforming process from sheet metal is investigated for the materials Cu-OFE and AA6014 with regard to the basic feasibility and the occurrence of size effects. The results reveal that the process chain is basically suitable to produce metallic micro parts with a high repeatability. Size effects are identified during the process. Since several studies postulate that size effects can be minimised by scaling down the metallic grain structure, the grain size of the aluminium material AA6014-W is scaled down to less than one micrometre by using an accumulative roll bonding process (ARB). Subsequently, the effects of the ultrafine grain (UFG) structure on the forming process are analysed. It could be shown that a strengthened material state increases the material utilization. Furthermore, too soft materials can cause damage on the part during ejection. The occurring size effects cannot be eliminated by reducing the grain size.