Effect of Al₂TiO₅ Content and Sintering Temperature on the Microstructure and Residual Stress of Al₂O₃-Al₂TiO₅...

A series of Al₂O₃-Al₂TiO₅ ceramic composites with different Al₂TiO₅ contents (10 and 40 vol.%) fabricated at different sintering temperatures (1450 and 1550 °C) was studied in the present work. The microstructure, crystallite structure, and through-thickness residual stress of these composites were investigated by scanning electron microscopy, X-ray diffraction, time-of-flight neutron diffraction, and Rietveld analysis. Lattice parameter variations and individual peak shifts were analyzed to calculate the mean phase stresses in the Al₂O₃ matrix and Al₂TiO₅ particulates as well as the peak-specific residual stresses for different hkl reflections of each phase. The results showed that the microstructure of the composites was affected by the Al₂TiO₅ content and sintering temperature. Moreover, as the Al₂TiO₅ grain size increased, microcracking occurred, resulting in decreased flexure strength. The sintering temperatures at 1450 and 1550 °C ensured the complete formation of Al₂TiO₅ during the reaction sintering and the subsequent cooling of Al₂O₃-Al₂TiO₅ composites. Some decomposition of AT occurred at the sintering temperature of 1550 °C. The mean phase residual stresses in Al₂TiO₅ particulates are tensile, and those in the Al₂O₃ matrix are compressive, with virtually flat through-thickness residual stress profiles in bulk samples. Owing to the thermal expansion anisotropy in the individual phase, the sign and magnitude of peak-specific residual stress values highly depend on individual hkl reflection. Both mean phase and peak-specific residual stresses were found to be dependent on the Al₂TiO₅ content and sintering temperature of Al₂O₃-Al₂TiO₅ composites, since the different developed microstructures can produce stress-relief microcracks. The present work is beneficial for developing Al₂O₃-Al₂TiO₅ composites with controlled microstructure and residual stress, which are crucial for achieving the desired thermal and mechanical properties.