Impact of Fabrication Techniques and Polishing Procedures on Surface Roughness of Denture Base Resins
Published on: January 17, 2025
Optical and mechanical properties of conventional, milled and 3D-printed denture teeth
Mei Ting Tieh1, John Neil Waddell1, Joanne Jung Eun Choi1
1Sir John Walsh Research Institute, Faculty of Dentistry, University of Otago, 310 Great King Street, Dunedin, 9016, New Zealand.
Objectives:
Investigate the effect of various liquids on the optical properties and Vickers hardness of conventional, milled and 3D-printed denture teeth.
Methods:
Six different types of denture teeth (Maxillary anteriors of three different conventional teeth, Vivodent DCL, SR Phonares II, Vita Physiodens; milled teeth, IvotionDent; and two different 3D-printed teeth, Asiga DentaTooth and NextDent C&B MFH) were investigated (total n = 336). The labial surface of each specimen was prepared to a dimension of 10 × 5 × 3mm. Specimens were immersed in artificial saliva, coffee, red wine and denture cleaner with artificial aging to simulate denture use of 12 and 24 months in vivo. Measurements of translucency parameter (TP), shade change (ΔE), surface roughness (Ra) and Vickers hardness (VHN) were conducted at baseline and after artificial aging while immersed in the liquids at each timeframe. Data were statistically analysed by ANOVA and post-hoc test (SPSS Ver 27). Surfaces of specimens were analysed under scanning electron microscopy (SEM).
Results:
Milled teeth had the highest overall translucency parameter (5.33 ± 0.76-7.3 ± 0.99). All materials had statistically significant change in translucency parameter and shade after 24 months simulated aging (p < 0.05), especially the milled and 3D-printed teeth (p < 0.01). Surface roughness of all materials were under plaque accumulation threshold Ra = 0.2 μm. At baseline, Vita Physiodens teeth (PMMA with microfillers) demonstrated the highest hardness (33.99 kgf/mm2±3.7), whereas both 3D-printed materials exhibited the lowest hardness (13.27 kgf/mm2±0.36-18.13 kgf/mm2±0.93). Artificial saliva, red wine and denture cleaner had a statistically significant impact (p < 0.05) on hardness of all materials (12.1 kgf/mm2±1.17-30.77 kgf/mm2±2.98).
Conclusions:
Milled teeth exhibited the best optical properties (highest overall translucency parameter and lowest shade change). Milled teeth were also the only material that showed colour change (ΔE values) within clinically acceptable limits. Denture cleaner had the most impact on optical and mechanical properties of all materials. Surface roughness and hardness of 3D-printed teeth had the most change after artificial aging.
More Related Videos
07:42Quasistatic Mechanical Testing for Computer-Aided Design and Manufacturing Occlusal Veneers Cemented to Milled Dentin Analog Material
Published on: December 20, 2024
06:16Author Spotlight: Establishing an Accurate Microhardness Testing Protocol for Craniofacial Tissues
Published on: April 26, 2024
Related Concept Videos
01:21Tooth Anatomy
The Crown, Neck, and Root
The visible part of the tooth is referred to as the crown. It's covered by enamel, the hardest substance in the human body. The crown is uniquely shaped for each type of tooth, allowing for different functions such as cutting, tearing, or...
01:15Teeth
In the bud stage, the tooth germ (an aggregation of cells) starts to form in the developing jawbone. During the cap stage, the tooth germ differentiates into enamel organ, dental papilla, and dental sac, which will later develop into the tooth's enamel, dentin...