Oxidation Level and Glycidyl Ether Structure Determine Thermal Processability and Thermomechanical Properties of...

Developing flexible, stretchable, and thermally processable materials for packaging and stretchable electronic applications from polysaccharide-based polymers contributes to the smooth transition of the fossil-based economy to the circular bioeconomy. We present arabinoxylan (AX)-based thermoplastics obtained by ring-opening oxidation and subsequent reduction (dA-AX) combined with hydrophobization with three different glycidyl ethers [n-butyl (BuGE), isopropyl (iPrGE), and 2-ethyl hexyl (EtHGE) glycidyl ether]. We also investigate the relationship between structural composition, thermal processing, and thermomechanical properties. BuGE- and iPrGE-etherified dA-AXs showed glass-transition temperatures (T_g) far below their degradation temperatures and gave thermoplastic materials when compression-molded at 140 °C. The BuGE (3 mol)-etherified dA-AX films at 19 and 31% oxidation levels show 244% (±42) and 267% (±72) elongation, respectively. In contrast, iPrGE-dA-AX samples with shorter and branched terminals in the side chains had a maximum of 60% (±19) elongation. No studies have reported such superior elongation of AX thermoplastic films and its relationship with molar substitution and T_g. These findings have implications on the strategic development of chemical modification routes using commercial polymer processing technologies and on fine-tuning structures and properties when specific polysaccharide-based polymers are used to engineer bio-based products for film, packaging, and substrates for stretchable electronic applications.