Revealing the compressive and flow properties of novel bone scaffold structure manufactured by selective laser...

Additive manufacturing is revolutionizing the field of medical sciences through its key application in the development of bone scaffolds. During scaffold fabrication, achieving a good level of porosity for enhanced mechanical strength is very challenging. The bone scaffolds should hold both the porosity and load withstanding capacity. In this research, a novel structure was designed with the aim of the evaluation of flexible porosity. A CAD model was generated for the novel structure using specific input parameters, whereas the porosity was controlled by varying the input parameters. Poly Amide (PA 2200) material was used for the fabrication of bone scaffolds, which is a biocompatible material. To fabricate a novel structure for bone scaffolds, a Selective Laser Sintering machine (SLS) was used. The displacement under compression loads was observed using a Universal Testing Machine (UTM). In addition to this, numerical analysis of the components was also carried out. The compressive stiffness found through the analysis enables the verification of the load withstanding capacity of the specific bone scaffold model. The experimental porosity was compared with the theoretical porosity and showed almost 29% to 30% reductions when compared to the theoretical porosity. Structural analysis was carried out using ANSYS by changing the geometry. Computational Fluid Dynamics (CFD) analysis was carried out using ANSYS FLUENT to estimate the blood pressure and Wall Shear Stress (WSS). From the CFD analysis, maximum pressure of 1.799 Pa was observed. Though the porosity was less than 50%, there was not much variation of WSS. The achievement from this study endorses the great potential of the proposed models which can successfully be adapted for the required bone implant applications.