Interfacial reactions in lithia-based cathodes depending on the binder in the electrode and salt in the electrolyte

Lithia (Li₂O)-based cathodes, utilizing oxygen redox reactions for obtaining capacity, exhibit higher capacity than commercial cathodes. However, they are highly reactive owing to superoxides formed during charging, and they enable more active parasitic (side) reactions at the cathode/electrolyte and cathode/binder interfaces than conventional cathodes. This causes deterioration of the electrochemical performance limiting commercialization. To address these issues, the binder and salt for electrolyte were replaced in this study to reduce the side reaction of the cells containing lithia-based cathodes. The commercially used polyvinylidene fluoride (PVDF) binder and LiPF₆ salt in the electrolyte easily generate such reactions, and the subsequent reaction between PVDF and LiOH (from decomposition of lithia) causes slurry gelation and agglomeration of particles in the electrode. Moreover, the fluoride ions from PVDF promote side reactions, and LiPF₆ salt forms POF₃ and HF, which cause side reactions owing to hydrolysis in organic solvents containing water. However, the polyacrylonitrile (PAN) binder and LiTFSI salt decrease these side reactions owing to their high stability with lithia-based cathode. Further, thickness of the interfacial layer was reduced, resulting in decreased impedance value of cells containing lithia-based cathodes. Consequently, for the same lithia-based cathodes, available capacity and cyclic performance were increased owing to the effects of PAN binder and LiTFSI salt in the electrolyte.