On the Potential of a Poly(vinylidenefluoride-co-hexafluoropropylene) Polymer Inclusion Membrane Containing Aliquat^®...

A polymer inclusion membrane (PIM) composed of 50 wt% base polymer poly(vinylidenefluoride-co-hexafluoropropylene), 40 wt% extractant Aliquat^® 336, and 10 wt% dibutyl phthalate as plasticizer/modifier provided the efficient extraction of vanadium(V) (initial concentration 50 mg L^-1) from 0.1 M sulfate solutions (pH 2.5). The average mass and thickness of the PIMs (diameter 3.5 cm) were 0.057 g and 46 μm, respectively. It was suggested that V(V) was extracted as VO₂SO₄^- via an anion exchange mechanism. The maximum PIM capacity was estimated to be ~56 mg of V(V)/g for the PIM. Quantitative back-extraction was achieved with a 50 mL solution of 6 M H₂SO₄/1 v/v% of H₂O₂. It was assumed that the back-extraction process involved the oxidation of VO₂⁺ to VO(O₂)⁺ by H₂O₂. The newly developed PIM, with the optimized composition mentioned above, exhibited an excellent selectivity for V(V) in the presence of metallic species present in digests of spent alumina hydrodesulfurization catalysts. Co-extraction of Mo(VI) with V(V) was eliminated by its selective extraction at pH 1.1. Characterization of the optimized PIM was performed by contact angle measurements, atomic-force microscopy, energy dispersive X-ray spectroscopy, thermogravimetric analysis/derivatives thermogravimetric analysis and stress-strain measurements. Replacement of dibutyl phthalate with 2-nitrophenyloctyl ether improved the stability of the studied PIMs.