Spider-web-inspired membrane reinforced with sulfhydryl-functionalized cellulose nanocrystals for oil/water...

The cellulose nanocrystals (CNC) has attracted widespread attention in reinforced materials. However, the application of CNC in electrospinning has been limited due to its self-polymerization. Herein, a cobweb-like nanofibrous membrane was fabricated by electrospinning the polyacrylonitrile (PAN) and sulfydryl-functionalized CNC (SC). The SC content could reach to 48 wt% after the thiolation modification. The membrane with ultrafine fibers and interlaced nets possessed outstanding porosity (91.7%) and underwater superoleophobicity. An ultrahigh permeation flux of 1244 L·m^-2·h^-1 with a separation efficiency of >99.9% was achieved driven by gravity. The mechanical properties also enhanced significantly with the increase of SC. When the addition amount of SC was 48 wt%, the maximum tensile stress was 2.9 MPa, which was 3.4 times than that of the PAN membrane. The antifouling performance and chemical stability endowed the SC(48)/PAN membrane with intriguing reusability, thus making it exhibit enormous potential in oil/water separation.