Citric Acid-Mediated Microwave-Hydrothermal Synthesis of Mesoporous F-Doped HAp Nanorods from Bio-Waste for Biocidal
Gopalu Karunakaran1, Eun-Bum Cho1, Govindan Suresh Kumar2
1Institute for Applied Chemistry, Department of Fine Chemistry, Seoul National University of Science and Technology (Seoul Tech), Gongneung-ro 232, Nowon-gu, Seoul 01811, Korea.
Abstract:
In this current research, mesoporous nano-hydroxyapatite (HAp) and F-doped hydroxyapatite (FHAp) were effectively obtained through a citric acid-enabled microwave hydrothermal approach. Citric acid was used as a chelating and modifying agent for tuning the structure and porosity of the HAp structure. This is the first report to use citric acid as a modifier for producing mesoporous nano HAp and F-doped FHAp. The obtained samples were characterized by different analyses. The XRD data revealed that F is incorporated well into the HAp crystal structure. The crystallinity of HAp samples was improved and the unit cell volume was lowered with fluorine incorporation. Transmission electron microscopy (TEM) images of the obtained samples revealed that a nano rod-like shape was obtained. The mesoporous structures of the produced HAp samples were confirmed by Brunauer-Emmett-Teller (BET) analysis. In vivo studies performed using zebrafish and C. elegans prove the non-toxic behavior of the synthesized F doped HAp samples. The obtained samples are also analyzed for antimicrobial activity using Gram-negative and Gram-positive bacteria, which are majorly involved in implant failure. The F doped samples revealed excellent bactericidal activity. Hence, this study confirms that the non-toxic and excellent antibacterial mesoporous F doped HAp can be a useful candidate for biocidal implant application.