Influence of Laser Beam Power on Microstructure and Microhardness of Fe/ZrC Coatings Produced on Steel Using Laser...

This paper presents preliminary tests of the parameter analysis of the Fe/ZrC coatings production process and the obtained properties. The effects of laser beam power on the obtained microstructure, chemical composition and microhardness were investigated. The tests consisted of the production of composite coatings by laser processing of initial coatings made in the form of a paste on a steel substrate. During the tests, a diode laser with a rated power of 3 kW was used. The laser processing process was carried out using a constant scanning speed laser beam of 3 m/min and four different powers of the laser beam: 500 W, 700 W, 900 W, 1100 W. It was found that it is possible to create composite coatings on a steel surface, where the matrix is made of iron-based alloy and the reinforcing phase is ZrC carbide. It was also found that reinforcing phase content decreased as laser beam power increased. A similar relationship was found for microhardness. As laser beam power increases, the microhardness of the iron-based matrix decreases, finally reaching a value lower than the heat-affected zone. It was found that the amount of hard carbide phases in the iron-based matrix affects the total hardness of the coatings. Presented study concern Fe/ZrC coatings that have not previously been produced on steel by laser processing of precoating, which may be a new contribution in the field of metal surface engineering.