Effects of the Surface Structure on the Water Transport Behavior in PEMFC Carbon Fiber Papers
Tongqing Qu1, Xiyi Huang1, Biao Wang1
1State Key Laboratory for Modification of Chemical Fibers and Polymer Materials, College of Materials Science and Engineering, Donghua University, Shanghai 201620, P. R. China.
Abstract:
In this paper, three kinds of carbon fiber papers (CFPs), including pure CFP, poly(tetrafluoroethylene) (PTFE)-treated CFP (PTFE-CFP), and microporous layer (MPL)-coated CFP (MPL-CFP), were used to investigate the effects of the surface structure on the water transport behavior in CFPs. Compared to pure CFP, applying PTFE on the CFP increases the breakthrough pressure by 0.2 times, while it decreases the water flow rate at initial penetration by 0.06 times, owing to the strong hydrophobicity of PTFE-CFP. The pore diameter of MPL-CFP reduces sharply after coating the MPL, which leads to increasing breakthrough pressure by 0.6 times. The Young-Laplace equation is applied to study the relationship between the structure (wettability and pore-size distribution) of CFPs and the water transport behavior (breakthrough pressure), and the results show that in addition to wettability and pore size, the pore-size gradient also plays a crucial role in water transport.