Dimethyl Sulfoxide Dentin Pretreatments Do Not Improve Bonding of a Universal Adhesive in Etch-and-Rinse or Self-etch...

To evaluate the influence of dimethyl sulfoxide (DMSO) solutions used as dentin pretreatments on microtensile bond strength (µTBS), as well as the dentin/restoration interface micromorphology of a universal adhesive in etch-and-rinse or self-etch mode.

Eighty blocks of dentin were submitted to acid conditioning with 35% phosphoric acid (etch-and-rinse), or not (self-etch), and distributed among the treatments (n = 10): CON: Scotchbond Universal/3M Oral Care; DMSO: pretreatment with DMSO; DMSO/water: pretreatment with DMSO in water (1:1); DMSO/ethanol: pretreatment with DMSO in ethanol (1:1). Microtensile bond strength and failure tests were performed after 24-h and 6-month storage. The tooth-restoration interface was evaluated using scanning electron microscopy to assess the hybrid layer formed.

The interaction between treatments, storage time, and etching modes was not significant for µTBS (p = 0.2469). The DMSO, DMSO/water and DMSO/ethanol pretreatments did not affect µTBS values at either time point (p = 0.8732). Aging decreased µTBS over time only for the etch-and-rinse strategy, although the groups presented higher microtensile bond strengths in etch-and-rinse mode than in self-etch mode at both time points (p < 0.0001). The micromorphological images of the interface showed that different DMSO pretreatment solutions did not impair hybrid layer formation.

The use of dentin pretreatments containing DMSO did not improve the bonding or the micromorphology of a universal adhesive in etch-and-rinse or self-etch modes.