Investigating the Recyclability of Laser PP CP 75 Polypropylene Powder in Laser Powder Bed Fusion (L-PBF)

In the present study, recyclability of Laser PP CP 75 polypropylene powder from Diamond Plastics GmbH was determined by characterizing and comparing the used powder after each cycle with material from previous cycles and with fresh powder. The melt flow index of Laser PP CP 75 was affected by recycling since it was observed to change by 30.62% after the 8th 100% re-use cycle, a lower value than PA 12 of 66.04%, for the 6th re-use cycle. Parts printed with virgin Laser PP CP 75 had an average dimensional error of 3.02% (virgin material) and 4.06% after the 4th 100% re-use cycle, which raises concerns about the commercial viability of the material. After the 4th re-use cycle, the printed parts had distorted edges and failed to print after the 9th print cycle. Lastly, tensile testing revealed a skewed bell-shaped curve of strength versus the number of recycles with the highest ultimate tensile strength occurring for the second 100% re-use cycle (7.4 MPa). The curves for elastic modulus and percentage elongation were inverted with minimum points for the 2nd 100% re-use cycle. Overall, the experimental work confirmed that the properties of polypropylene powder were affected by recycling in polymer laser sintering, but the powder exhibited superior characteristics upon recycling to those of the predominantly used PA 12 powder.