Microstructure and Thermal Deformation Behavior of Hot-Pressing Sintered Zr-6Al-0.1B Alloy

Zr-6Al-0.1B alloy rich in Zr₃Al phase is prepared by hot-pressing sintering. The thermal deformation behavior of sintered Zr-6Al-0.1B is analyzed by isothermal compression tests at deformation temperatures of 950, 1050, and 1150 °C with strain rates of 0.01, 0.1, and 1 s^-1. The results indicate that at the early stage of thermal deformation, the stress increases rapidly with the increase of strain and then reaches the peak value. Subsequently, the stress decreases with the increase of strain under the softening effect. On the whole, the true stress-strain curve shifts to the high stress area with the increase of strain rate or the decrease of deformation temperature, so the sintered Zr-6Al-0.1B alloy belongs to the temperature and strain rate sensitive material. For the microstructure evolution of sintered Zr-6Al-0.1B during the isothermal compression, the high strain rate can improve the grain refinement. However, because sintered Zr-6Al-0.1B is a low plastic material, too high strain rate will exceed the deformation capacity of the material, resulting in an increase in defects. The increase of deformation temperature also contributes to grain refinement, but when the temperature is too high, due to the decomposition of Zr₃Al phase, the deformation coordination of the material decreases, leading to the increase of the probability of the occurrence of defects. This study verified the feasibility of hot-pressing sintering to prepare Zr-6Al-0.1B alloy rich in Zr₃Al phase and laid the foundation of "hot-pressing sintering + canning hot-extrusion" process of Zr-6Al-0.1B alloy components.