Increasing the Stability of Metal-Organic Frameworks by Coating with Poly(tetrafluoroethylene)

When compared to industrially stable zeolites, the instability of metal-organic frameworks (MOFs) has been denounced by researchers. Boosting the stability of existing MOFs is highly important for practical applications. In this report, we develop a new strategy to prepare MOFs/poly(tetrafluoroethylene) (PTFE) composites, which can highly improve the chemical, pressure, and photostabilities of zeolitic imidazolate framework (ZIF)-8. Composite materials were prepared by a physical blending of ZIF-8 and PTFE emulsion with different ratios and annealing at 370 °C. Transmission electron microscopy (TEM) studies reveal that the nanoparticles of ZIF-8 are coated by PTFE to form the composite materials. Upon mixing with 20 or 50 wt % PTFE, the ZIF-8/PTFE materials show a superhydrophobic property with water contact angles of around 156°. Pristine ZIF-8 is not stable in water with stirring under acidic, basic, and irradiation conditions, while the ZIF-8/PTFE materials are stable under the same conditions. The ZIF-8/PTFE materials can also maintain their crystalline structure after being compressed with a 10 MPa pressure, while pristine ZIF-8 changes to an amorphous solid after the same pressure treatment. Using water as a solvent, ZIF-8/PTFE can be used as a highly efficient and recyclable catalyst for Knoevenagel reaction at room temperature. The successful preparation of stable ZIF-8/PTFE composite materials provides a useful method to enhance the chemical, pressure, and photostabilities of MOFs.