Effect of thickness on color appearance of multilayer CAD/CAM composite resin blocks

The aim of this study was to evaluate the effect of thickness on the color appearance and translucency parameter (TP) of multilayer CAD/CAM composite resin blocks. Four brands of A3-shade multilayer CAD/CAM composite resin blocks were examined (Katana Avencia, CERASMART Multi, KZR-CAD HR Block 4 E-va, and Block HC Hard AN). Six specimens of five thicknesses were prepared for each brand, yielding 120 specimens in total. CIEL*a*b* values were determined using a spectrophotometer against black and white backgrounds, and the TP was calculated. The color differences (ΔE₀₀) between layers (cervical/middle/incisal) and brands for each thickness against the black background were calculated using the CIEDE2000 system. As a result, on the black background, L* of the incisal layer was greater while a* and b* were smaller than those of the cervical layer for all brands. The ΔE₀₀ values between the cervical and middle layers (1.23-3.27) were smaller than those between the cervical and incisal layers (3.98-5.67) and those between the middle and incisal layers (3.14-5.92). TP decreased with increasing block thickness. Some TP differences between layers were significant, but they were less than 2.75. In conclusion, the color appearance of CAD/CAM blocks was significantly influenced by both the thickness and layer. L*a*b* decreased with thickness, and a negative exponential relationship between TP and thickness was observed for all layers and brands.