Effects of Hydrofluoric Acid Concentration and Etching Time on the Bond Strength to Ceramic-coated Zirconia

To evaluate the effects of different hydrofluoric acid (HF) concentrations and etching times on the surface topography, roughness, and resin bond strength to ceramic-coated zirconia (CC), and to compare them with the effects of alumina air-abrasion combined with 10-MDP (AA).

AA and CC specimens were divided into 12 groups (N = 10). The CC groups were etched with HF at different concentrations (5% or 9.5%) for various durations (0 min, 1 min, 2 min, 3 min, 5 min or 10 min). The surface morphology was analyzed using SEM. Energy-dispersive x-ray spectroscopy (EDS) and x-ray diffraction (XRD) were performed for chemical and crystalline-phase analyses. Surface roughness (Ra) and shear bond strength (SBS) were recorded and statistically analyzed.

The SBS of CC groups initially increased, but then decreased with etching time for both HF acid concentrations. The 9.5% HF group displayed more marked topographical changes and higher Ra compared with the 5% HF group for the same etching period. Mean SBS was lower in the AA group compared with the CC groups etched with 5% HF for 2-10 min and 9.5% HF for 1-3 min (p < 0.05).

Different HF concentrations and etching times influenced the surface topography, roughness, and resin bond strength of/to ceramic-coated zirconia. Etching with 5% HF for 5 min and with 9.5% HF for 2 min, respectively, provided the highest SBS.