Novel polymethyl methacrylate modified with metal methacrylate monomers: biological, physicomechanical, and optical
Georgia Arla Cabrera Khader1, Andressa da Silva Barboza1, Juliana Silva Ribeiro1
1Graduate Program in Dentistry, Federal University of Pelotas, Pelotas, Brazil.
Abstract:
This study sought to evaluate the physical and antimicrobial properties of a thermopolymerizable acrylic resin (PMMA) modified with metallic methacrylate monomers -zirconia (ZM), tin (TM), and di-n-butyl (DNTMB) methacrylates. Color stability was evaluated before and after immersion of samples in a staining solution by a digital spectrophotometer. The mechanical brushing test was evaluated by the roughness test. The flexural strength test used a mechanical testing machine. Human keratinocytes were used to assess cell viability and the biofilm formation assay was carried out for 5 days, in a microcosms model after one year of specimen storage. For statistical analysis, the method chosen was based on adherence to the normal distribution model and equality of variances (p < 0.05). The addition of DNTMB to PMMA promoted great antimicrobial action, acceptable cytocompatibility, without hampering the physical-mechanical properties of the commercial material. Therefore, the modified PMMA proved to be a promisor alternative to conventional resins.This study sought to evaluate the physical and antimicrobial properties of a thermopolymerizable acrylic resin (PMMA) modified with metallic methacrylate monomers -zirconia (ZM), tin (TM), and di-n-butyldimethacrylate-tin (DNTMB) methacrylates. Color stability was evaluated before and after immersion of samples in a staining solution using a digital spectrophotometer. The mechanical brushing test was evaluated by the roughness test. The flexural strength test used a mechanical testing machine. Human keratinocytes were used to assess cell viability and the biofilm formation assay was carried out for 5 days in a microcosm model after one year of specimen storage. For statistical analysis, the method chosen was based on adherence to the normal distribution model and equality of variances (p < 0.05). The addition of DNTMB to PMMA promoted great antimicrobial action, acceptable cytocompatibility, without hampering the physical-mechanical properties of the commercial material. Therefore, the modified PMMA proved to be a promising alternative to conventional denture base resins for dental use.