2D-2D lattice engineering route for intimately coupled nanohybrids of layered double hydroxide and potassium...

2D-2D lattice engineering route is used to synthesize intimately coupled nanohybrids of layered double hydroxide (LDH) and potassium hexaniobate. The 2D-2D lattice engineering route is based on the electrostatically derived self-assembly of delaminated zinc-chromium-layered double hydroxide (ZC-LDH) nanosheets and potassium hexaniobate (HNb) nanosheets (ZCNb nanohybrids). The 2D-2D lattice-engineered ZCNb nanohybrids display expanded surface area, mesoporous anchored nanosheets network morphology, and intimate coupling between nanosheets. The 2D-2D lattice engineered ZCNb nanohybrids are used for the low temperature operated gas sensor. The ZCNb nanohybrids display outstanding selectivity for the SO₂, with the high response of 61.5% compared to pristine ZC-LDH (28.08%) and potassium niobate (8%) at 150 °C. Moreover, ZCNb sensors demonstrate superior response and recovery periods of 6 and 167 s at 150 °C, respectively. This result underscores the exceptional functionality of the ZCNb nanohybrids as efficient SO₂ sensors. Moreover, these findings vividly demonstrate that the 2D-2D lattice-engineered ZCNb nanohybrids are quite effective not only in improving the gas sensor activity but also in developing of new type of intimately coupled mesoporous LDH-metal-oxide based hybrid materials.