Enhancement of Proton Conductivity Performance in High Temperature Polymer Electrolyte Membrane, Processed the Adding...

A pyridobisimidazole unit was introduced into a polymer backbone to obtain an increased doping level, a high number of interacting sites with phosphoric acid and simple processibility. The acid uptake of poly(pyridobisimidazole) (PPI) membrane could reach more than 550% (ADL = 22), resulting in high conductivity (0.23 S·cm^-1 at 180 °C). Along with 550% acid uptake, the membrane strength still held 10 MPa, meeting the requirement of Proton Exchange Membrane (PEM). In the Fenton Test, the PPI membrane only lost around 7% weight after 156 h, demonstrating excellent oxidative stability. Besides, PPI possessed thermal stability with decomposition temperature at 570 °C and mechanical stability with a glass transition temperature of 330 °C.