Modification of Hydrogenation and Corrosion Properties of Hydrogen Storage Material by Amorphous TiCrFeCoNi HEA Layer

The effect of encapsulation of LaNi_4.5Co_0.5 powdered hydrogen storage material with ≈0.5 µm thick, magnetron-sputtered amorphous film of TiCrFeCoNi high-entropy alloy (HEA) on functional hydrogenation parameters of the hydride electrode is discussed. The multicycle galvanostatic charge/discharge tests carried out in deaerated, 6 M KOH solution allow for determining specific capacity decrease, exchange current density of the H₂O/H₂ system, and high rate discharge ability (HRD) of the hydride electrodes. Concentrations of individual constituents of the HEA in the particle coating determined by EDS analysis were practically the same (≈20 at.%) as in the applied TiCrFeCoNi target material. The XRD phase analysis pointed out the amorphous structure of the HEA coating. The presence of HEA coating decreases capacity by 10-15 per cent, but increases exchange current density for H₂O/H₂ system. The effect of HEA on capacity fade is ambiguous: low for 10-25 cycles (most probably due to effective corrosion inhibition) and distinct at long-term cycling (most probably due to galvanic effects resulting from mechanical degradation of particle surface). The presence of HEA coating considerably improves the HRD of the electrode material: for a discharge rate of 5C, the HRD coefficient becomes 4.6 times greater for HEA modified storage material.