Study on the Properties and Mechanism of Magnesium Oxychloride Adhesive Particleboard Modified by Fly Ash

Magnesium oxychloride adhesive (MOA) is a kind of inorganic adhesive with a low energy consumption and environmental protection. The modified particleboard with magnesium oxychloride adhesive (MOPB) has the advantages of no volatiles and has a high mechanical strength. In this study, MOA and poplar shavings were used to prepare MOPB, fly ash (FA) was used to modify and enhance the properties of MOPB; the influence mechanism on the mechanical of MOPB was studied. Fourier transform infrared spectroscopy (FTIR) and X-ray diffraction (XRD) were used to analysis the bonding mechanism of MOA and poplar shavings, and the composite system model of MOPB was constructed. The mechanism of modified MOPB with FA (MOPB-FA) was clarified. The results show that the use of FA effectively improved the mechanical strength of MOPB, and when the ratio of FA addition was 15 wt%, MOPB-FA's modulus of rupture (MOR) value was 16.32 MPa, an increase of 24.5% more than before (13.11 MPa). The modulus of elasticity (MOE) value was 4595.51 MPa, an increase of 76.7% more than before (2600 MPa), and the thickness of swelling (TS) value was 0.35%, a decrease of 85.2% less than before (2.36%).