Characterization of Al₂O₃ Matrix Composites Fabricated via the Slip Casting Method Using NiAl-Al₂O₃ Composite Powder

This work aimed to characterize Al₂O₃ matrix composites fabricated by the slip casting method using NiAl-Al₂O₃ composite powder as the initial powder. The composite powder, consisting of NiAl + 30 wt.% Al₂O₃, was obtained by mechanical alloying of Al₂O₃, Al, and Ni powders. The composite powder was added to the Al₂O₃ powder to prepare the final powder for the slip casting method. The stained composite samples presented high density. EDX and XRD analyses showed that the sintering process of the samples in an air atmosphere caused the formation of the NiAl₂O₄ spinel phase. Finally, the phase composition of the composites changed from the initial phases of Al₂O₃ and NiAl to Al₂O₃, Ni, and NiAl₂O₄. However, in the area of Ni, fine Al₂O₃ particles remaining from the initial composite powder were visible. It can be concluded that after slip casting, after starting with Al₂O₃ and the composite powder (NiAl-Al₂O₃) and upon sintering in air, ceramic matrix composites with Ni and NiAl₂O₄ phases, complex structures, high-quality sintered samples, and favorable mechanical properties were obtained.