Influence of Mo on the Microstructure and Corrosion Behavior of Laser Cladding FeCoCrNi High-Entropy Alloy Coatings

FeCoCrNi and FeCoNiCrMo_0.2 high-entropy alloy powders were prepared by gas atomization. Two kinds of coatings were prepared on the surface of 304 stainless steel by laser cladding technology. The effect of Mo element on the microstructure of laser cladding FeCoCrNi coating and its corrosion behavior in 3.5 wt.% NaCl solution was investigated. Both FeCoCrNi and FeCoCrNiMo_0.2 powders exhibit a single-phase FCC structure. Due to the remelting and multiple heat treatments during the preparation of the laser cladding coating, a small amount of σ and μ phases appeared in the FeCoCrNiMo_0.2 coating. The microstructures of the two coatings from the bonding area to the top layer are planar, columnar and equiaxed grains, respectively. The addition of the Mo element causes the dendrite size in the middle region of the FeCoCrNiMo_0.2 coating increases significantly and exhibits obvious orientation characteristics. FeCoCrNiMo_0.2 coating has high corrosion potential (-0.01 V_SHE) and low current density (0.94 × 10^-7 A/cm²) in 3.5 wt.% NaCl solution, showing excellent corrosion resistance. The passivation film formed on corroded the FeCoCrNiMo_0.2 coating contains high content of oxides of Cr and Mo. The addition of the Mo element enhances the compactness and pitting resistance of the passivation film.