Effectiveness of non-uniform thickness on a locking compression plate used as a biodegradable bone implant plate

Conventional locking compression plate (LCP) made of non-biodegradable materials are well-known bone implants for internal fracture fixation because of their proven experimental success. LCP, however, is mechanically underpowered when made up of biodegradable materials (even with Mg-alloy). The biodegradable implant plate should not only exhibit adequate mechanical performance during implantation but also perform well after fracture, at least until complete healing of the fractured bone. With the aim of achieving enhanced mechanical performance, the design of the LCP has been modified to the design of Biodegradable Locking Compression Plate (BLCP) by adding a suitable thickness in the middle (only 4.6% of the total volume of the LCP), which may help retain some additional strength during implantation and after degradation. Both BLCP and LCP have been comparatively analyzed via FEM with the aid of axial compression and four-point bending tests. BLCP has a better mechanical capability of withstanding loads in its degraded form than in its non-degradable form. Furthermore, BLCP is up to 15.83% mechanically better in the non-degraded form as compared to LCP, which again becomes up to 100% more mechanically adequate in the degraded forms of BLCP than in LCP. BLCP is found safe for degradation up to 2 mm or 6 months with an estimated degradation rate of 4 mm/year, which may allow it to support fractured bone for at least the standard healing time. BLCP can be considered as a superior biodegradable bone implant plate after experimental assurance with the physiological environment and may replace LCP.