Synthesis and characterization of polyaniline-hydrotalcite-graphene oxide composite and application in polyurethane
Boi An Tran1,2, Huynh Thanh Linh Duong1, Thi Xuan Hang To3,2
1Institute of Chemical Technology, Vietnam Academy of Science and Technology 1A TL29, Thanh Loc Ward, District 12 Ho Chi Minh City Vietnam tban@ict.vast.vn.
Abstract:
In this paper, a composite from polyaniline and graphene oxide-hydrotalcite hybrid (PAN-HG) was fabricated by direct polymerization of aniline using ammonium persulphate as an oxidant in the presence of a HG hybrid. The structure and morphological properties of synthesized PAN-HG composites were characterized by Fourier transform infrared (FTIR) spectroscopy, X-ray diffraction (XRD), Raman spectra, and scanning electron microscopy (SEM) techniques. The electrochemical properties of the composite particles were also analyzed by potentiodynamic polarization curves to evaluate the corrosion inhabitation. The results were calculated by Tafel fitting and showed that the effective corrosion protection values were 73.11%, 88.46%, and 95.49%, corresponding to HG, 1PAN-HG, and 2PAN-HG. The influence of PAN-HG on the corrosion protection of the polyurethane coating applied on the CT3 steel was investigated. As a result, the PU containing 0.5% of 2PAN-HG showed the most effective protection of the CT3 steel substrate. The R C of the coating was about 1.61 × 107 Ω cm2, and after immersion for 30 days, the R C value was 0.17 × 106 Ω cm2. From all the analyzed results, PAN-HG has enhanced the corrosion protection and a complicated protection mechanism was also concluded and explained.