Dopamine-derived cavities/Fe₃O₄ nanoparticles-encapsulated carbonaceous composites with self-generated...

Dopamine-derived cavities/Fe₃O₄ nanoparticles-encapsulated carbonaceous composites with self-generating three-dimensional (3D) network structure were successfully fabricated by a facile synthetic method, in which sodium alginate provided carbon matrix pores and excellent microwave absorption performance was established. The hollow cavities derived from the core-shell-like CaCO₃@polydopamine were creatively introduced into the 3D absorber to significantly improve the absorption performance. The sample calcined at 700 °C exhibited the most outstanding microwave absorption performance, with minimal reflection loss up to -50.80 dB at 17.52 GHz with a rare thickness of only 1.5 mm when filler loading was 35% in paraffin matrix. The effective absorption bandwidth of reflection loss < -10 dB reached 3.52 GHz from 14.48 GHz to 18 GHz, corresponding to the same thickness of 1.5 mm. In contrast, the sample without hollow dopamine-derived cavities showed poor performance due to poor impedance matching, and this highlights the role of hollow cavities brought into the 3D structure, which led to a difference in interfacial polarization, multiple reflections and scattering. The novel dopamine-derived cavities/Fe₃O₄ nanoparticles-encapsulated carbonaceous composites with 3D network structure can be regarded as a promising candidate for application as a microwave absorber with strong absorption.