Effects of Charcoal Toothpaste on the Surface Roughness, Color Stability, and Marginal Staining of Resin Composites

This study was designed to evaluate the effects of charcoal toothpaste on the surface roughness, color stability, and marginal staining of resin composite restorations.

A total of 100 bovine incisors was collected. The crowns were sectioned and randomly divided into 10 groups (n=10) according to two study factors: toothpaste groups and nanoparticle resin composite groups. Five toothpastes-Bianco Pro Clinical (Bianco Oral Care, Uberlândia, MG, Brazil) - Control group; Bianco Carbon (Bianco Oral Care); NAT, Natural Suavetex Carvão Ativado (Suavetex, Uberlândia, MG, Brazil); Nano Action Black Be Emotion (Polishop, Jundiaí, SP, Brazil); and BIW, Black is White (Curaprox, Curaden AG, Kriens, Switzerland)-and two resin composites-Z350XT (Filtek Z350XT, 3M Oral Care) and Vittra (Vittra APS FGM, Joinville, SC, Brazil)-were used. Circular cavities with a diameter of 4 mm and a depth of 1 mm were prepared on the buccal face of the tooth crowns and restored with resin composites. The specimens were subjected to three months of simulated toothbrushing. The surface roughness (right angle [Ra], in micrometers [μm]) of the resin composites was measured before and after toothbrushing in five areas per specimen. The resin composite color and luminosity changes (ΔE and ΔL, respectively) were measured using reflectance spectroscopy (Vita EasyShade). Macro photographs were taken before and after toothbrushing to qualitatively analyze the marginal staining (MSt) of the resin composite restorations. Scanning electron microscopy (SEM) was performed before and after the simulated toothbrushing. Ra data were analyzed using two-way analysis of variance with repeated measures and the Tukey HSD test; MSt was analyzed using Kruskal-Wallis and Dunn tests (α=0.05), and the resin composite color change was analyzed using the clinically unacceptable level of ΔE > 3.3.

Simulated brushing increased Ra irrespective of the resin composite or toothpaste used. No significant differences were found in Ra between the control group and all groups on which the charcoal toothpastes were tested. A clinically unacceptable level of resin composite color change (ΔE>3.3) was found after the use of most charcoal toothpastes. Use of Bianco Carbon resulted in marginal staining similar to that of the control group and was lower than that of the other charcoal toothpastes. Vittra brushed with black toothpaste showed the highest marginal staining.

Use of charcoal toothpaste resulted in Ra values of resin composites similar to those found with conventional toothpastes. Charcoal toothpaste generally resulted in clinical resin composite color changes (ΔE). All charcoal toothpastes, except Bianco Carbon, caused marginal staining of the resin composite restorations.