Incorporation of chlorhexidine in self-adhesive resin cements

The aim of this study was to evaluate the maximum amount of chlorhexidine (CHX) that could be incorporated to self-adhesive resin cements to add antibacterial effect without affecting the physical properties. The CHX was incorporated into a commercial self-adhesive resin cement at mass fractions of 0.5-15 wt%, and the CHX-release profile, antibacterial effect, flexural and bond strengths of experimental cements were evaluated. Increasing the CHX content from 5 to 15 wt% resulted in a higher released concentration of CHX. In agar diffusion tests, experimental cements containing 5, 10, and 15 wt% CHX produced inhibition zones against oral bacteria. In flexural strength and shear bond strength to dentin, no significant reduction was observed with the incorporation of 5 wt% CHX. This in vitro study suggests that the addition of 5 wt% CHX yielded an antibacterial self-adhesive cement and had no adverse effect on the flexural and shear bond strengths.