Super Tough, Ultrastretchable, and Thermoresponsive Hydrogels with Functionalized Triblock Copolymer Micelles as
Yuan-Na Sun1, Guo-Rong Gao1, Gao-Lai Du1
1Polymers and Composites Division, Ningbo Institute of Materials Technology and Engineering, Chinese Academy of Sciences, 1219 Zhongguan West Road, Ningbo 315201, China.
Abstract:
Vinyl-functionalized thermosensitive Pluronic F127 micelles have been used as multifunctional cross-links for the synthesis of super tough, highly resilient and thermoresponsive nanomicelle (NM) hydrogels. Pluronic F127 diacrylate (F127DA) with vinyl groups on both ends self-assembled in aqueous solution into micelles. Such micelles served as multifunctional macro-cross-links to copolymerize with acrylamide (AAm) monomers, generating novel NM hydrogels with extraordinary tensile and compressive properties, without using any chemical cross-linkers. Uniaxial tensile tests demonstrated a fracture strain above 2265%, an ultimate stress of 276 kPa, and a fracture energy of 2.34 MJ/m3. Under compression tests, these hydrogels did not fracture up to 98% strain and 62 MPa stress. Cyclic compressive loading-unloading tests at 90% strain showed no decay of the hyseteresis energy, indicating an unprecedented fatigue resistance.
More Related Videos
08:39Magnetic and Thermal-sensitive PolyN-isopropylacrylamide-based Microgels for Magnetically Triggered Controlled Release
Published on: July 4, 2017
09:09Synthesis of PolyN-isopropylacrylamide Janus Microhydrogels for Anisotropic Thermo-responsiveness and Organophilic/Hydrophilic Loading Capability
Published on: February 27, 2016