Two-body wear of occlusal splint materials from subtractive computer-aided manufacturing and three-dimensional
Felix Schmeiser1, Uwe Baumert2, Bogna Stawarczyk3
1Dental Material Unit, Department of Prosthetic Dentistry, Dental School, University Hospital, LMU Munich, Goethestraße 70, 80336, Munich, Germany. felix.schmeiser@med.uni-muenchen.de.
Objectives:
To investigate the two-body wear of occlusal splint materials fabricated from subtractive computer-aided manufacturing (CAM) compared to three-dimensional printing (3DP).
Material And Methods:
Forty-eight substrates (n = 12/material) in the design of a mandibular first molar were fabricated using CAM (CAM-TD, Thermeo, pro3dure medical GmbH, Iserlohn, Germany; CAM-CL, CLEARsplint, Astron Dental Corporation, Lake Zurich, USA) and 3DP (3DP-GI, GR22 flex, pro3dure medical GmbH; 3DP-KY, KeySplint soft, Keystone Industries, Gibbstown, USA). The substrates were subjected to mastication simulation (120,000 cycles, 37 °C, 50 N, 1.3 Hz) opposed to enamel antagonists. The two-body wear was measured through matching of the scanned substrates before and after aging using Gaussian best-fit method. The damage patterns were categorized and evaluated based on microscopic examinations. Data was analyzed using Kolmogorov-Smirnov test followed by 1-way analysis of variance (ANOVA). Pearson correlation was calculated between vertical and volumetric material loss. The failure types were analyzed with Chi2-test and Ciba Geigy table.
Results:
No difference in two-body wear results between all materials was found (p = 0.102). Fatigue substrates showed a perforation for CAM and a fracture for 3DP. No abrasion losses on the antagonists were detected.
Conclusions:
3DP substrates showed no differences in two-body wear compared to CAM ones but are more likely to show a fracture. None of the tested materials caused an abrasion on human teeth structure.
Clinical Relevance:
While therapies with occlusal splint materials are rising, 3DP offers a promising alternative to CAM in terms of production accuracy and therapeutic success at reduced costs.