One-Step Synthesis of Healable Weak-Polyelectrolyte-Based Hydrogels with High Mechanical Strength, Toughness, and
1State Key Laboratory of Supramolecular Structure and Materials, College of Chemistry, Jilin University, Changchun 130012, P. R. China.
Abstract:
Excellent self-recovery is critically important for soft materials such as hydrogels and shape memory polymers. In this work, weak-polyelectrolyte-based hydrogels with high mechanical strength, toughness, healability, and excellent self-recovery are fabricated by one-step polymerization of acrylic acid and poly(ethylene glycol) methacrylate in the presence of oppositely charged branched polyethylenimine. The synergy of electrostatic and hydrogen-bonding interactions and the in situ formed polyelectrolyte complex nanoparticles endow the hydrogels with a tensile strength of ∼4.7 MPa, strain at break of ∼1200%, and toughness of ∼32.6 MJ m-3. The hydrogels can recover from an ∼300% strain to their initial state within 10 min at room temperature without any external assistance. Moreover, the hydrogels can heal from physical cut at room temperature and exhibit a prominent shape-memory performance with rapid shape recovery speed and high shape-fixing and shape-recovery ratios.