Mechanical and Metallurgical Evaluation of 3 Different Nickel-Titanium Rotary Instruments: An In Vitro and In...

An in-depth evaluation of the mechanical and metallurgical properties of NiTi instruments is fundamental to assess their performance and to compare recently introduced instrument with widespread ones. According to this, since there are no data on this topic, the aim of the study was to mechanically and metallurgically evaluate an instrument recently introduced into the market (ZenFlex (ZF)), by comparing it with two well-known instruments with similar characteristics: Vortex Blue (VB) and EdgeSequel Sapphire (EES). According to this, 195 instruments were selected: 65 ZF, 65 VB and 65 EES. Each group was divided in subgroups according to the mechanical tests (i.e., cyclic fatigue resistance, torsional resistance and bending ability; (n = 20)) and the metallurgical test (differential scanning calorimetry (n = 5)). A scanning electron microscopy was performed to verify the causes of fracture after mechanical tests (cyclic fatigue and torsional tests). According to results, VB showed the highest flexibility and cyclic fatigue resistance in comparison to the other instruments, with a statistically significant difference (p < 0.05). Regarding torsional resistance, EES showed the lowest value of torque at fracture, with a statistically significant difference, whilst the comparison between ZF and VB showed no statistically significant difference (p > 0.05). DSC analysis pointed out that VB had the highest austenite start and finish temperatures, followed by ESS and then ZF. ESS sample showed the highest martensite start and finish temperatures followed by VB and ZF. Considering the results, it can be concluded that VB showed the best mechanical performance during static tests in comparison to ESS and ZF. This is fundamentally due to the interaction of parameters such as instrument design and heat-treatments that are able to enhance its mechanical performance.