Investigation of the process intergrowth of bone tissue into the hole in titanium implants (Experimental research)

Despite the use of modern implants, complications such as nonunion and avascular necrosis of the femoral head are observed in femoral neck fractures (FNF). We have created a new perforated I-beam implant for FNF osteosynthesis and developed a new osteosynthesis philosophy based not only on the mechanical and biomechanical interaction of the bone-implant system, but also on the interaction of the biological properties of the bone and the implant. The purpose of the work is to study the interaction of the biological process of the bone - its regeneration (germination) of bone tissue into the holes of the implant.

The experiment was carried out on fourteen Chinchilla rabbits in accordance with all international standards. A perforated implant specially made of titanium (ChM, Poland) was surgically implanted into the proximal femur. The implant measurements were as follows: length - 6 mm, width - 3 mm, thickness - 2 mm, 2 holes with a diameter of 2 mm. The 14 rabbits were divided into 7 groups. After 1, 2, 3, 4, 5, 10 and 12 weeks the animals were withdrawn from the experiment according to the standard rules in sequential order. The preparations were placed in a formalin solution and sent to the pathomorphology laboratory (CITO, Russia) for histological studies.

Weekly histopathological studies revealed a gradual transition from the organization of a hematoma to the formation of mature bone tissue in the holes of the implants. The titanium implant is bioinert and did not cause any visible reactions from the bone tissue. Simultaneous integration of vascular proliferation and newly formed bone tissue into the implant holes were revealed. On 10-12-week preparations, the formation of trabecular structures of mature bone tissue was revealed in the holes of the implants and elements of adipose and bone marrow tissue were observed. Macroscopic examination of 4-5-week preparations showed almost complete filling of the holes with bone tissue. On 10-12-week preparations, the bone tissue in the holes of the implants did not differ from the bone tissue surrounding the implant. The processes of formation of mature bone tissue in the holes of the implants were similar to the processes of physiological bone healing (regeneration) at the fracture site.

The obtained results show the following: 1.The titanium implant is bioinert and does not cause any visible reactions from the bone tissue; 2. There is a gradual process of formation of new vessels, and then the formation of new bone tissue in the holes of the implant instead of the one damaged during implantation. Thus, the results of this experiment indirectly confirm our assumption that a perforated implant for FNF osteosynthesis will participate not only in the mechanical and biomechanical interaction of the bone-implant system, but will also include the 3rd element in this system - the biological properties of the bone itself. We assume that these properties of the new implant will increase blood flow in the femoral neck and partially replenish the volume of bone tissue destroyed during osteosynthesis which does not occur with FNF osteosynthesis by any of the known implants.