Stress Triaxiality in Anisotropic Metal Sheets-Definition and Experimental Acquisition for Numerical Damage...

Governing void growth, stress triaxiality (η) is a crucial parameter in ductile damage prediction. η is defined as the ratio of mean stress to equivalent stress and represents loading conditions. Attempts at introducing material anisotropy in ductile damage models have started only recently, rendering necessary in-depth investigation into the role of η here. η is commonly derived via finite elemnt (FE) simulation. An alternative is presented here: based on analytical expressions, η is obtained directly from the strains in the critical zone. For anisotropic materials, η associated with a specimen varies with yield criterion and material (anisotropy). To investigate the meaning of triaxiality for anisotropic materials, metal sheets made of dual phase steel DP780, and zirconium alloy Zirlo are chosen. Analytical expressions for η are derived for three popular yield criteria: von Mises, Hill48 and Barlat89. Tensile tests are performed with uniaxial tension, notch, and shear specimens, and the local principal strains, measured via digital image correlation (DIC), are converted to h. The uniaxial tension case reveals that only the anisotropic yield criteria can predict the expected η = 1/3. The ramifications associated with anisotropy become apparent for notched specimens, where η differences are highest; for shear specimens, the yield criterion and material-dependence is relatively moderate. This necessitates η and, consequently, the triaxiality failure diagram (TFD) being accompanied by the underlying yield criterion and anisotropy parameters. As the TFD becomes difficult to interpret, it seems more advantageous to provide pairs of principal strain ratio β and failure strain. Suggestions for deriving representative β and η are made.