Solvent-free preparation of thermoplastic bio-materials from microcrystalline cellulose (MCC) through reactive
Pei Yang1, Ming Yan1, Chaochao Tian1
1Jiangsu Co-Innovation Center of Efficient Processing and Utilization of Forest Resources, Jiangsu Provincial Key Lab of Pulp and Paper Science and Technology, College of Light Industry and Food, Nanjing Forestry University, Nanjing 210037, China.
Abstract:
Cellulose, as a renewable biopolymer, was acknowledged as a promising alternative for petroleum polymer. However, the poor thermoplasticity of cellulose caused a limitation in its full development. Herein, a solvent-free and simple strategy was proposed for the preparation of thermoplastic bio-materials from microcrystalline cellulose (MCC). Kraft lignin (KL) was employed as a plasticizer in this work. It was demonstrated that MCC-based materials with great thermoplasticity and mechanical properties could be successfully prepared by reactive extrusion. The obtained MCC-based material ML8G (with 50 wt% KL adding) possessed great thermostability and thermoplastic properties with an obvious glass transition temperature (Tg) at 106 °C. In addition, the bending strength, flexural modulus and storage modulus of the MCC-based material were improved to 20.44 MPa, 3139.47 MPa and 5.81 GPa respectively. Furthermore, the obtained MCC-based material exhibited good water stability and biodegradability. The comprehensive results confirmed the feasibility of MCC-based materials plasticized with KL through reactive extrusion. Overall, this work was a promising development in the field of bio-plastic utilization of natural products from a green source.