This paper summarizes the assessment of directional anisotropy in local mechanical properties for Laser Powder Bed Fusion (LPBF) IN-718 bulk samples via the use of miniature samples excised from the bulk for both as-deposited and post-treated states. The quasi-static tensile properties at room temperature are investigated at several different locations along the build direction and at different orientations for both considered states. A comparison between the excised miniature tensile specimens and standard-sized sample results have also been conducted and exhibit very good agreement. Significant anisotropy is present in mechanical properties at different build heights for the as-deposited state, while the post-treated material exhibited more homogenous properties, both along the height and for different sampling orientations. However, significant reductions (e.g., >30%) in the strength (Yield, UTS) along with a significant increase in the reduction in area at fracture is found for post-processed materials. Metallography and fractography analyses were conducted in order to begin to determine the source(s) of this anisotropy for the as-deposited state.