Synergistic Treatment of Congo Red Dye with Heat Treated Low Rank Coal and Micro-Nano Bubbles

In this study, the adsorption method and micro-nano bubble (MNB) technology were combined to improve the efficiency of organic pollutant removal from dye wastewater. The adsorption properties of Congo red (CR) on raw coal and semi-coke (SC) with and without MNBs were studied. The mesoporosity of the coal strongly increased after the heat treatment, which was conducive to the adsorption of macromolecular organics, such as CR, and the specific surface area increased greatly from 2.787 m²/g to 80.512 m²/g. MNBs could improve the adsorption of both raw coal and SC under different pH levels, temperatures and dosages. With the use of MNBs, the adsorption capacity of SC reached 169.49 mg/g, which was much larger than that of the raw coal at 15.75 mg/g. The MNBs effectively reduced the adsorption time from 240 to 20 min. In addition, the MNBs could ensure the adsorbent maintained a good adsorption effect across a wide pH range. The removal rate was above 90% in an acidic environment and above 70% in an alkaline environment. MBs can effectively improve the rate of adsorption of pollutants by adsorbents. SC was obtained from low-rank coal through a rapid one-step heating treatment and was used as a kind of cheap adsorbent. The method is thus simple and easy to implement in the industrial context and has the potential for industrial promotion.