Stain Susceptibility of Composite Resins: Pigment Penetration Analysis

Composite resins are considered the material of choice for esthetic direct restorations, considering both their satisfying esthetic and mechanical properties. The success of composite resin restorations depends highly on their color stability. Discoloration causes color mismatch, consequent patient dissatisfaction, and eventually additional costs for correction/replacement of the restoration. The purpose of this study was to evaluate the degree of pigment penetration within the composite resins, in order to understand how discoloration can be treated properly. Two different commercially available composite resins were compared in the study: a nano-filled composite resin and a non-homogeneous micro-hybrid composite resin. A coffee solution was used to induce staining of the materials. Subsequently, the penetration of the pigments was measured by analyzing the color from the outside to the inside of the specimen. 14 levels were analyzed starting from 0.1 mm to 3.0 mm in depth. The ANOVA test demonstrated a statistically significant difference (p < 0.0001) between test and control groups up to a depth of 1.0 mm for the nano-filled composite and up to a depth of 2.0 mm for the non-homogeneous micro-hybrid composite. The two composite resin materials, subjected to pigmenting treatment, underwent a color variation with different patterns.