A Comparative Study of Several Properties of Plywood Bonded with Virgin and Recycled LDPE Films

In this work, to better understand the bonding process of plastic plywood panels, the effects of recycled low-density polyethylene (rLDPE) film of three thicknesses (50, 100, and 150 µm) and veneers of four various wood species (beech, birch, hornbeam, and poplar) on the properties of panels were studied. The obtained properties were also compared with the properties of plywood panels bonded by virgin low-density polyethylene (LDPE) film. The results showed that properties of plywood samples bonded with rLDPE and virgin LDPE films differ insignificantly. Samples bonded with rLDPE film demonstrated satisfactory physical and mechanical properties. It was also established that the best mechanical properties of plywood are provided by beech veneer and the lowest by poplar veneer. However, poplar plywood had the best water absorption and swelling thickness, and the bonding strength at the level of birch and hornbeam plywood. The properties of rLDPE-bonded plywood improved with increasing the thickness of the film. The panels bonded with rLDPE film had a close-to-zero formaldehyde content (0.01-0.10 mg/m²·h) and reached the super E0 emission class that allows for defining the laboratory-manufactured plastic-bonded plywood as an eco-friendly composite.