Novel Hybrid Nanomaterials Based on Poly-N-Phenylanthranilic Acid and Magnetic Nanoparticles with Enhanced Saturation...

A one-step preparation method for cobalt- and iron-containing nanomaterials based on poly-N-phenylanthranilic acid (P-N-PAA) and magnetic nanoparticles (MNP) was developed for the first time. To synthesize the MNP/P-N-PAA nanocomposites, the precursor is obtained by dissolving a Co (II) salt in a magnetic fluid based on Fe3O4/P-N-PAA with a core-shell structure. During IR heating of the precursor in an inert atmosphere at T = 700−800 °C, cobalt interacts with Fe3O4 reduction products, which results in the formation of a mixture of spherical Co-Fe, γ-Fe, β-Co and Fe3C nanoparticles of various sizes in the ranges of 20 < d < 50 nm and 120 < d < 400 nm. The phase composition of the MNP/P-N-PAA nanocomposites depends significantly on the cobalt concentration. The reduction of metals occurs due to the hydrogen released during the dehydrogenation of phenylenamine units of the polymer chain. The introduction of 10−30 wt% cobalt in the composition of nanocomposites leads to a significant increase in the saturation magnetization of MNP/P-N-PAA (MS = 81.58−149.67 emu/g) compared to neat Fe3O4/P-N-PAA (MS = 18.41−27.58 emu/g). The squareness constant of the hysteresis loop is κS = MR/MS = 0.040−0.209. The electrical conductivity of the MNP/P-N-PAA nanomaterials does not depend much on frequency and reaches 1.2 × 10−1 S/cm. In the argon flow at 1000 °C, the residue is 77−88%.