Sb-doped Li₁₀GeP₂S₁₂-type electrolyte Li₁₀SnP_2-xSb_xS₁₂ with enhanced ionic conductivity and lower lithium-ion...

Li₁₀SnP₂S₁₂ (LSPS) has been regarded as a promising solid electrolyte because of its higher ionic conductivity and lower cost. In this work, P sites of LSPS are partially substituted with Sb by the solid-phase sintering method. A series of Li₁₀SnP_2-xSb_xS₁₂ (0 ≤ x ≤ 0.4) solid electrolytes are prepared. Among them, the ionic conductivity of the Li₁₀SnP_1.8Sb_0.2S₁₂ solid electrolyte reaches 2.43 mS cm^-1. Through X-ray diffraction and refinement analysis, it is found that Sb successfully substituted part of P and increased the lattice constant. Through temperature-dependent alternating current impedance experiments and density functional theory calculations, it is found that the main reasons for the increase in ionic conductivity are the reduction of activation energy and the energy barrier of the Li⁺ migration path around Sb. The improved air stability of the electrolyte after Sb doping conforms to the Hard-Soft-Acid-Base theory. Furthermore, the assembled all-solid-state battery with Li₁₀SnP_1.8Sb_0.2S₁₂ exhibits a high specific capacity and good cycling stability than LSPS.