Absorption-Dominant, Low-Reflection Multifunctional Electromagnetic Shielding Material Derived from Hydrolysate of...

High-performance flexible conductive films are highly promising for the development of wearable devices, artificial intelligence, medical care, etc. Herein, a three-step procedure was developed to produce electromagnetic interference (EMI) shielding, Joule heating, and a hydrophobic nanofiber film based on hydrolysate of waste leather scraps (HWLS): (i) electrospinning preparation of the HWLS/polyacrylonitrile (PAN)/zeolitic imidazolate framework-67 (ZIF-67) nanofiber film, (ii) carbonization of the HWLS/PAN/ZIF-67 nanofiber film, and (iii) coating of the carbon nanofiber@cobalt (Co@CNF) nanofiber film with perfluorooctyltriethoxysilane (POTS). The X-ray diffraction results showed that metal nanoparticles and amorphous carbon had obvious peaks. The micromorphology results showed that metal nanoparticles were coated with carbon nanofibers. The conductivity and shielding efficiency of the carbon nanofiber film with 250 μm thickness could reach 45 S/m and 49 dB, respectively, and absorption values (A > 0.5) were higher than reflection (R) values for the Co@CNF nanofiber film, which indicated that the contribution of absorption loss was more significant than that of reflection loss. Ultrafast electrothermal response performances were also achieved, which could guarantee the normal functioning of films in cold conditions. The water contact angle of the Co@CNF@POTS nanofiber film was ∼151.3°, which displayed a self-cleaning property with water-proofing and antifouling. Absorption-dominant and low-reflection EMI shielding and electrothermal films not only showed broad application potential in flexible wearable electronic devices but also provided new avenues for the utilization of leather solid waste.