Tuning Electro-Magnetic Interference Shielding Efficiency of Customized Polyurethane Composite Foams Taking Advantage...

Electromagnetic interference (EMI) has been recognized as a new sort of pollution and can be considered as the direct interference of electromagnetic waves among electronic equipment that frequently affects their typical efficiency. As a result, shielding the electronics from this interfering radiation has been addressed as critical issue of great interest. In this study, different hybrid nanocomposites consisting of magnetite nanoparticles (Fe₃O₄) and reduced graphene oxide (rGO) as (conductive/magnetic) fillers, taking into account different rGO mass ratios, were synthesized and characterized by XRD, Raman spectroscopy, TEM and their magnetic properties were assessed via VSM. The acquired fillers were encapsulated in the polyurethane foam matrix with different loading percentages (wt%) to evaluate their role in EMI shielding. Moreover, their structure, morphology, and thermal stability were investigated by SEM, FTIR, and TGA, respectively. In addition, the impact of filler loading on their final mechanical properties was determined. The obtained results revealed that the Fe₃O₄@rGO composites displayed superparamagnetic behavior and acceptable electrical conductivity value. The performance assessment of the conducting Fe₃O₄@rGO/PU composite foams in EMI shielding efficiency (SE) was investigated at the X-band (8-12) GHz, and interestingly, an optimized value of SE -33 dBw was achieved with Fe₃O₄@rGO at a 80:20 wt% ratio and 35 wt% filler loading in the final effective PU matrix. Thus, this study sheds light on a novel optimization strategy for electromagnetic shielding, taking into account conducting new materials with variable filler loading, composition ratio, and mechanical properties in such a way as to open the door for achieving a remarkable SE.